Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere
Mathan, M. Bobby, Raja, V.S., and Mukhopadhyay, A.K. (2004) Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere. Scripta Materialia, 51 (11). pp. 1075-1079.
![[img]](https://researchonline.jcu.edu.au/style/images/fileicons/application_pdf.png) |
PDF (Published Version)
Restricted to Repository staff only |
Abstract
The purpose of this work is to show that during slow strain rate testing (SSRT), the laboratory air might not be a non-corrosive atmosphere for evaluating the Iscc (stress corrosion cracking susceptibility index) of high strength Al alloys. Instead, it is proposed that glycerin could be effectively used as the non-corrosive atmosphere to find out the correct Iscc. This is demonstrated while examining 7010 Al alloy in the under aged condition.
| Item ID: | 9554 |
|---|---|
| Item Type: | Article (Research - C1) |
| ISSN: | 1872-8456 |
| Keywords: | 7010 Al alloy; stress corrosion cracking index; slow strain rate testing |
| Date Deposited: | 27 Apr 2010 23:22 |
| FoR Codes: | 09 ENGINEERING > 0912 Materials Engineering > 091207 Metals and Alloy Materials @ 100% |
| SEO Codes: | 86 MANUFACTURING > 8611 Basic Metal Products (incl. Smelting, Rolling, Drawing and Extruding) > 861101 Basic Aluminium Products @ 100% |