Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7 ceramics - a low temperature sintered material for LTCC applications
Jacob, Mohan V., Sudheendran, K., and Raju, K.C. James (2010) Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7 ceramics - a low temperature sintered material for LTCC applications. Journal of the Australian Ceramic Society, 46 (2). pp. 54-58.
PDF (Published Version)
- Published Version
Restricted to Repository staff only |
Abstract
Ceramic samples with low sintering temperature were prepared by solid state reaction from the respective high purity oxide powders. Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7 were sintered below 900 degree Celcius and the density is above 90%. The frequency dependent dielectric properties of these ceramics up to 1MHz were measured using Agilent 4294A impedance analyser. The dielectric properties of Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7ceramics with x = 0 to 0.4 were estimated at microwave frequencies from room temperature to 15 K using Dielectric Post (DP) resonator techniques. The high dielectric permittivity together with the low sintering temperature will make this material an attractive candidate for LTCC applications.
Item ID: | 16760 |
---|---|
Item Type: | Article (Research - C1) |
ISSN: | 0004-881X |
Keywords: | dielectric materials, dielectric constant, loss tangent, LTCC |
Date Deposited: | 12 May 2011 01:58 |
FoR Codes: | 09 ENGINEERING > 0912 Materials Engineering > 091201 Ceramics @ 100% |
SEO Codes: | 97 EXPANDING KNOWLEDGE > 970109 Expanding Knowledge in Engineering @ 100% |
Downloads: |
Total: 3 |
More Statistics |