Hydrogen-induced-cracking in magnesium alloy under cathodic polarization
Kannan, M. Bobby, Dietzel, W., Raman, R.K. Singh, and Lyon, P. (2007) Hydrogen-induced-cracking in magnesium alloy under cathodic polarization. Scripta Materialia, 57 (7). pp. 579-581.
![[img]](https://researchonline.jcu.edu.au/style/images/fileicons/application_pdf.png) |
PDF (Published Version)
Restricted to Repository staff only |
View at Publisher Website: http://dx.doi.org/10.1016/j.scriptamat.2...
56
7
Abstract
The hydrogen-induced-cracking (HIC) behaviour of the magnesium alloy AZ80 was evaluated using the slow strain rate test method. The study shows no evidence of HIC in AZ80 alloy after pre-exposure or pre-charging in distilled water. However, under continuous charging in distilled water during straining, the AZ80 alloy shows evidence of HIC. The contradiction reported in the literature is addressed.
| Item ID: | 9559 |
|---|---|
| Item Type: | Article (Research - C1) |
| ISSN: | 1872-8456 |
| Keywords: | magnesium alloys; hydrogen embrittlement; corrosion; slow strain rate test |
| Date Deposited: | 10 Apr 2010 01:22 |
| FoR Codes: | 09 ENGINEERING > 0912 Materials Engineering > 091207 Metals and Alloy Materials @ 100% |
| SEO Codes: | 86 MANUFACTURING > 8611 Basic Metal Products (incl. Smelting, Rolling, Drawing and Extruding) > 861199 Basic Metal Products (incl. Smelting, Rolling, Drawing and Extruding) not elsewhere classified @ 100% |
| Downloads: |
Total: 7 |
| More Statistics |
Actions (Repository Staff Only)
 |
Item Control Page |